CPE Film
High heat sealing strength
High toughness
Food contact grade
Low coefficient of friction
Product Advantages
Category
|
Product Category |
Product Type |
|---|---|
| Laminating grade | CPE |
| sauce pouch packaging grade | ESP |
| Inflatable grade | EA2 |
| Flexible and toughness grade | EF |
| Low static grade | ELE |
| Low absorption grade | ELA |
| Matt grade | EMT |
| Tissue packaging grade | ED |
Note: The above CPE film can be customized for clients according to their specific application demand.
Performance
| CPE Laminating grade E2 | ||||||
|---|---|---|---|---|---|---|
| Property | Unit | Typical Values | Reference | Method | ||
| Thickness | μm | 40.0 | 100.0 | +/- 3.5% | GB/T 6672 | |
| Density | g/cm3 | 0.92 | 0.92 | +/- 2% | GB/T 1033.1 | |
| Weight | g/m2 | 36.8 | 92.0 | +/- 2% | GB/T 6672 | |
| Yield | m2/kg | 27.2 | 10.7 | +/- 2% | GB/T 6672 | |
| Tensile strength | MD | N/mm2 | 30 | 29 | ≥120 | GB/T 1040.3 |
| TD | N/mm2 | 23 | 25 | ≥200 | GB/T 1040.3 | |
| Elongation at break | MD | % | 792 | 1430 | ≤240 | GB/T 1040.3 |
| TD | % | 1288 | 1643 | ≤80 | GB/T 1040.3 | |
| Coefficient of Friction | Corona treated side | - | 0.51 | 0.53 | ≤0.25 | GB/T 10006 |
|
Non-corona treated side |
- | 0.20 | 0.18 | ≤0.25 | GB/T 10006 | |
| Sealing strength | N/15mm | 9.5 | 9.8 | ≥2.5 | QB/T 5609 | |
| Haze | % | 3.2 | 5.6 | ≤2.5 | GB/T 2410 | |
| Wetting tension (One side) | mN/m | 38 | 38 | ≥38 | GB/T14216-2008 | |
The information on Weifu products and their applications provided in this datasheet is based on testing of representative material and the results are believed to be reliable as at the date of publication advised below. The information does not constitute a warranty or guarantee, either expressly or implied, of any specific product attribute or the suitability of products for specific applications. For particular technical requirements or specifications, please contact Weifu.
Application
Suitable for seafood packaging, pet food packaging, small rice bags, inflated packing, flavour marinade packaging and so on. Recommended for BOPE/CPE lamination structures in order to make mono-olefinic structure. According to functional requirements, it can be also be laminated with other plastic films such as nylon, PET, BOPP, etc.